Bio-based Epoxy Resin System for Hot-melt Prepreg Curing at Mid-temperature

Xu Feng Zhang, Jin Guang Yu, Jia Hu Wei, Xiao Su Yi

Research output: Journal PublicationArticlepeer-review

3 Citations (Scopus)

Abstract

A novel bio-based epoxy resin system with rosin-sourced acid anhydrides was established by formula design and selection according to the resin film's forming performance and state with different storage time. The formula involves epoxy resin/curing agent/accelerator with mass proportion of 100/60/3-4. The curing property and the relationship between viscosity-temperature-time of resin were characterized by dynamic or steady state DSC analysis and cone plate viscometer, respectively. The results show the resin system can be cured at the range of 120-140℃, and the range of hot melt prepreg temperature is 60-85℃ with the viscosity from 1500mPa·s to 5000mPa·s. The processing time of hot melt prepreg is about 180min at 70℃. The curing mechanism of bio-based resin was also investigated through the samples with different curing time by IF and DSC.

Original languageEnglish
Pages (from-to)96-101
Number of pages6
JournalCailiao Gongcheng/Journal of Materials Engineering
Volume45
Issue number4
DOIs
Publication statusPublished - 20 Apr 2017
Externally publishedYes

Keywords

  • Bio-based
  • Cure at mid-temperature
  • Epoxy resin
  • Hot-melt prepreg

ASJC Scopus subject areas

  • Materials Science (miscellaneous)
  • Surfaces, Coatings and Films
  • Polymers and Plastics
  • Metals and Alloys

Fingerprint

Dive into the research topics of 'Bio-based Epoxy Resin System for Hot-melt Prepreg Curing at Mid-temperature'. Together they form a unique fingerprint.

Cite this