Preparation and characterization of a sulfonated carbon-based solid acid microspheric material (SCSAM) and its use for the esterification of oleic acid with methanol

Honglei Zhang, Xiang Luo, George Z. Chen, Feng He, Tao Wu

Research output: Journal PublicationArticlepeer-review

172 Downloads (Pure)

Abstract

In this study, a sulfonated group (-SO3H) rich carbon-based solid acid microspheric material was prepared by hydrothermal method followed by sulfonation using glucose as the raw material. Such a green, non-corrosive, and renewable carbon material was used as a heterogeneous catalyst for the esterification of oleic acid with methanol for the production of biodiesel. The carbon microspheres were characterized systematically. It was found that the carbon microspheres prepared under the optimal reaction conditions exhibited smooth surfaces, uniform particle sizes and good dispersion. The sulfonated carbon-based solid acid microspheric materials showed high acidity and good catalytic activities for the esterification of oleic acid with methanol. The influence of reaction operating conditions on the performance of esterification was studied. The optimal esterification reaction conditions were found to be: methanol/oleic acid molar ratio 12:1, catalyst loading 0.25 g (0.05 mmol H+), reaction temperature 65 °C, reaction time 8 h and mechanical stirring rate 360 rpm. It was found that the catalyst demonstrated very good reusability although there was noticeable loss in acidity due to the leaching of active sites.
Original languageEnglish
Pages (from-to)1024-1029
JournalAustin Chemical Engineering
Volume3
Issue number1
Publication statusPublished - 22 Feb 2016

Keywords

  • Biodiesel
  • Carbon-based material
  • Esterification
  • Reusability
  • Solid acid

Fingerprint

Dive into the research topics of 'Preparation and characterization of a sulfonated carbon-based solid acid microspheric material (SCSAM) and its use for the esterification of oleic acid with methanol'. Together they form a unique fingerprint.

Cite this