Finite Element Analysis of the Effects of Thermally Grown Oxide Thickness and Interface Asperity on the Cracking Behavior between the Thermally Grown Oxide and the Bond Coat

Jishen Jiang, Bingqian Xu, Weizhe Wang, Richard Amankwa Adjei, Xiaofeng Zhao, Yingzheng Liu

Research output: Journal PublicationArticlepeer-review

24 Citations (Scopus)

Abstract

Finite element simulations based on an interface cohesive zone model (CZM) have been developed to mimic the interfacial cracking behavior between the α-Al2O3 thermally grown oxide (TGO) and the aluminum-rich Pt-Al metallic bond coat (BC) during cooling from high temperature to ambient temperature. A two-dimensional half-periodic sinusoidal geometry corresponding to interface undulation is modeled. The effects of TGO thickness and interface asperity on the stress distribution and the cracking behavior are examined by parametric studies. The simulation results show that cracking behavior due to residual stress and interface asperity during cooling process leads to stress redistribution around the rough interface. The TGO thickness has strong influence on the maximum tensile stress of TGO and the interfacial crack development. For the sinusoidal asperities, there exists a critical amplitude above which the interfacial cracking is energetically favored. For any specific TGO thickness, crack initiation is dominated by the amplitude while crack propagation is restricted to the combine actions of the wavelength and the amplitude of the sinusoidal asperity.

Original languageEnglish
Article number022504
JournalJournal of Engineering for Gas Turbines and Power
Volume139
Issue number2
DOIs
Publication statusPublished - 1 Feb 2017
Externally publishedYes

Keywords

  • cohesive zone model
  • interface asperity
  • interfacial crack
  • thermally grown oxide

ASJC Scopus subject areas

  • Aerospace Engineering
  • Energy Engineering and Power Technology
  • Mechanical Engineering

Fingerprint

Dive into the research topics of 'Finite Element Analysis of the Effects of Thermally Grown Oxide Thickness and Interface Asperity on the Cracking Behavior between the Thermally Grown Oxide and the Bond Coat'. Together they form a unique fingerprint.

Cite this